SALOMON PERNOS
Lo mejor de Pernos
ESTRUTURAL

PERNERIA ESTRUCTURAL.
-
Perno Estructural ASTM A-325

NORMA ANSI/ASME B18.2.1 MATERIAL ACERO AL CARBONO TRATAMIENTO TERMICO : TEMPLE Y REVENIDO DUREZA 34 HRC Maximo RESISTENCIA 1000Mpa/102 Kg/mm2 ACABADO PAVONADO 1/2" 5/8" 3/4" 7/8" 1"

NORMA ANSI/ASME B18.2.1 MATERIAL ACERO AL CARBONO TRATAMIENTO TERMICO : TEMPLE Y REVENIDO DUREZA 34 HRC Maximo RESISTENCIA 1000Mpa/102 Kg/mm2 ACABADO PAVONADO 1/2" 5/8" 3/4" 7/8" 1"
-
Arandela Plana ASTM F-436

NORMA ASTM F-436 DUREZA 38-45 HRC ACABADO PAVONADO 1/2" 5/8" 3/4" 7/8" 1" 1 1/8" 1 1/4" 1 1/2"

NORMA ASTM F-436 DUREZA 38-45 HRC ACABADO PAVONADO 1/2" 5/8" 3/4" 7/8" 1" 1 1/8" 1 1/4" 1 1/2"
-
Tuerca Pesada 2H ASTM A-194 HDG

2H

2H
-
Tuerca Pesada 2H ASTM A -194

NORMA ANSI/ASME B18.2.2 MATERIAL ACERO AL CARBONO TRATAMIENTO TERMICO : TEMPLE Y REVENIDO DUREZA 38 HRC Maximo CARGA DE PRUEBA 123 Kg/mm2 ACABADO PAVONADO

NORMA ANSI/ASME B18.2.2 MATERIAL ACERO AL CARBONO TRATAMIENTO TERMICO : TEMPLE Y REVENIDO DUREZA 38 HRC Maximo CARGA DE PRUEBA 123 Kg/mm2 ACABADO PAVONADO

5/8" 3/4" 7/8" 1"

5/8" 3/4" 7/8" 1"
-
Perno Estructural A-325 H
-
Arandela Plana ASTM F-436

5/8" 3/4" 7/8" 1"

5/8" 3/4" 7/8" 1"
BARRA ROSCADA B7 ASTM A-193.
-
Barra Roscada B7 ASTM A-193

NORMA ASTM 193 B7 MATERIAL ACERO AL CARBONO TRATAMIENTO TERMICO : TEMPLE Y REVENIDO DUREZA 35 HRC RESISTENCIA 88 Kg./mm2 1/2" 5/8" 3/4" 7/8" 1" 1 1/2"-8 1 1/4"-8 1 3/8"-8 1 5/8"-8 1 3/4"-8 1 7/8"-8 2"-8 1/2" NC 5/8" NC 3/4" NC 7/8" NC 1" NC

NORMA ASTM 193 B7 MATERIAL ACERO AL CARBONO TRATAMIENTO TERMICO : TEMPLE Y REVENIDO DUREZA 35 HRC RESISTENCIA 88 Kg./mm2 1/2" 5/8" 3/4" 7/8" 1" 1 1/2"-8 1 1/4"-8 1 3/8"-8 1 5/8"-8 1 3/4"-8 1 7/8"-8 2"-8 1/2" NC 5/8" NC 3/4" NC 7/8" NC 1" NC